wheel refurb
iv noticed alot of people doing diy jobs on there wheels so think im going to have a go soon.. bit of a dab hand with can so fingers crossed,may go to gloss black.... maybe... any way was after general advice on what paints primers and and techniques is everyone using,or prefer, when doing there wheels, ill be taking the tyres off to do this aswell. thanks
__________________
"We're here for a good time, not a long time...." Colin McRae MBE 1968-2007" |
#2
|
||||
|
||||
Why???
Have it done properly with powder coat it will last a lot longer also .
__________________
Keep it on the black stuff and leave the pit boards alone |
#3
|
||||
|
||||
Quote:
halfords primer x4 cans halfords paint x4 cans halfords chip resistant lacqure x2 its a case of getting back to bare alloy or stripping off the lacqure fill kerb marks then rub back making sure you go through the grades of wetndry or your end up with lines once youve done that degrease the rims and wash and dry,prime up once dry wet sand the primer and reprime and wet sand till mint, when dry start spraying them up building up slowly! and wet sand if needed i used all the paint up left for a day or 2 ready for laqure, 2 coats of clear job done lol make use its warm and dry when you do it might pay to grab an alloy off connel to practice? or you can always go to aj for£37 a pop or ask russ £50 for a mint job!!!! i can always give a hand! might pay to ask scott for some info he just done a set of ultralights that steve now owns and there mint!
__________________
|
#4
|
||||
|
||||
Powdercoat....and have your wheels snap at some point.
__________________
2001 Bugeye - Project Black/Red, 1997 JDM Type R, 1995 V1 WRX, Defender Tithonus MOD Styleeee! |
#5
|
||||
|
||||
So thats why they are by the manufacturers ??
__________________
Keep it on the black stuff and leave the pit boards alone |
#6
|
||||
|
||||
__________________
2005 Spec B 6MT - KiDO tuned (~270Bhp)
Custom exhaust - Cosworth filter - Samco Intake - Tints - Bilstein B8/B6 & STI springs - SuperPro ALK - Whiteline positive shift kit, rack mounts, rear adjustable camber bushes, front ARB mounts & strut brace, 20mm rear ARB with AVO mounts, - Hardrace Gearbox and pitch mounts - Prodrive PFF7's - Front Brembos - Kenwood CarPlay - 1/2 carbon grille - STI front splitter |
#7
|
|||
|
|||
Never, been running them for years.
|
#8
|
||||
|
||||
Theyve been repaired before..not very well by the looks of it..so cant really make them worse.
Nice one neil.. Do you still need laquer on a solid colour?? Thought it was only metalics that need laquer..
__________________
"We're here for a good time, not a long time...." Colin McRae MBE 1968-2007" Last edited by munk; 01-03-2013 at 03:09 PM. |
#9
|
||||
|
||||
Quote:
__________________
"We're here for a good time, not a long time...." Colin McRae MBE 1968-2007" |
#10
|
||||
|
||||
You don't really need a lacquer on a solid colour but it will help resist chipping more than paint.
__________________
2005 Spec B 6MT - KiDO tuned (~270Bhp)
Custom exhaust - Cosworth filter - Samco Intake - Tints - Bilstein B8/B6 & STI springs - SuperPro ALK - Whiteline positive shift kit, rack mounts, rear adjustable camber bushes, front ARB mounts & strut brace, 20mm rear ARB with AVO mounts, - Hardrace Gearbox and pitch mounts - Prodrive PFF7's - Front Brembos - Kenwood CarPlay - 1/2 carbon grille - STI front splitter |
#11
|
||||
|
||||
not to sure on that mate i used it to stop it getting chipped if your goin to paint black chips are goin to notice i recon the colour uve got is tidy mate! why not try somthing nutty like a luminous orange lol im thinking of doin a set of rims the 350z bronze which i think would look smart but do a gunmetal first to dull the bronze down!
__________________
|
#12
|
||||
|
||||
Powder Coating involves re-heating an alloys that that already been heated, if the temp goes over 200, which is needed, the alloy, not just wheels, anything this applies too, becomes brittle from the inside and starts to crack.
The mixture of the alloy has to be an exact formulae, magnesium and silicon, for it not to crack. Can you guarantee they your wheels are made this way?
__________________
2001 Bugeye - Project Black/Red, 1997 JDM Type R, 1995 V1 WRX, Defender Tithonus MOD Styleeee! |
#13
|
||||
|
||||
A word of caution regarding the powder coating of aluminum.
Forged alloy wheels are desirable because they are known to be both strong and lightweight. To achieve these characteristics, they are typically manufactured from 6061-T6 grade aluminum. At some time during the manufacturing process this alloy must undergo a two-step thermal process in order for it to attain the desired mechanical properties, which include high strength and resistance to fatigue. These thermal processing or heat treating steps are known as solution treatment (985°F) and artificial aging (350°F). With forged 6061 aluminum, the artificial aging step requires the material to be held at 350°F for about 8 hours. The majority of powder coating materials require a cure temperature ranging from 300 to 400°F with a cure time of about 1 hour. Since this overlaps the temperature of the artificial aging step, the powder coating process has the potential to "overage" the aluminum causing embrittlement and reduced fatigue life. Recent advances in powder coating compounds have brought about lower cure temperatures of 250°F. These new powder coating compounds are more desirable, since they do not impact the prior thermal processing steps for heat treatable alloys such as 6061-T6 aluminum. When considering powder coating of heat treatable aluminum alloys (6000 and 7000 series), it is always advisable to confirm that the temperature of the part will not exceed 300°F. Ignoring this fact may result in a sudden and unexpected failure of a critical component. A critical failure in a forged alloy wheel could ruin not just one, but possibly the rest of your days. Before allowing someone to powder coat your forged aluminum wheels, ask them to use a lower cure temperature (250°F) compound and to maintain the temperature below 300°F at all times while they are processing your wheels. Additional reading: http://my.execpc.com/~davewrit/Powder.html
__________________
2005 Spec B 6MT - KiDO tuned (~270Bhp)
Custom exhaust - Cosworth filter - Samco Intake - Tints - Bilstein B8/B6 & STI springs - SuperPro ALK - Whiteline positive shift kit, rack mounts, rear adjustable camber bushes, front ARB mounts & strut brace, 20mm rear ARB with AVO mounts, - Hardrace Gearbox and pitch mounts - Prodrive PFF7's - Front Brembos - Kenwood CarPlay - 1/2 carbon grille - STI front splitter |
#14
|
||||
|
||||
Quote:
|
#15
|
||||
|
||||
__________________
"We're here for a good time, not a long time...." Colin McRae MBE 1968-2007" |
#16
|
||||
|
||||
its either this or a white set of rotors........cant decide
__________________
"We're here for a good time, not a long time...." Colin McRae MBE 1968-2007" |
#17
|
||||
|
||||
Which Rota's? Some stretch and poke action?
__________________
2001 Bugeye - Project Black/Red, 1997 JDM Type R, 1995 V1 WRX, Defender Tithonus MOD Styleeee! |
#18
|
||||
|
||||
Dark wheels, can't see white working on the WR1 really....
|
#19
|
||||
|
||||
__________________
"We're here for a good time, not a long time...." Colin McRae MBE 1968-2007" |
#20
|
||||
|
||||
mixed thoughts.can anyone get a bit of photo shop action on the go for me,pretty please, bit simple with a computer,unless its grot.
__________________
"We're here for a good time, not a long time...." Colin McRae MBE 1968-2007" |
#21
|
|||
|
|||
Big"E" tried white wheels once, looked proper ****e!
Last edited by alfa male; 04-03-2013 at 08:25 PM. |
#22
|
||||
|
||||
yeah its definetly had a mixed opinion.